1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500 mm), HRC45-48; Stredná forma (F300~500mm), HRC47-50; Malá vytláčacia matrica (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Osobitná pozornosť by sa mala venovať nasledujúcim bodom v procese tepelného spracovania vytláčacej hubice:
a. Rýchlosť ohrevu sekcie s vysokou teplotou by mala byť rýchla a doba zdržania by nemala byť príliš dlhá, aby sa zabránilo prepáleniu alebo prehriatiu vytláčacej formy. Prehriate -- hrubé zrná, prepálené -- prvky s nízkou teplotou topenia a inklúzia sa rozpustia;
b. Po ochladení včas temperujte hliníkovú extrúznu matricu, aby ste predišli prasklinám;
c. Keď sa po tepelnom spracovaní zistí, že tvrdosť vytláčacej hubice je nedostatočná alebo nerovnomerná, mala by sa žíhať a tepelné spracovanie by sa malo vykonať znova podľa procesu (keď je hodnota tvrdosti menšia ako HRC35, žíhanie nie je povolené a tepelné spracovanie sa vykonáva priamo);
d. V prípade veľkých hliníkových vytláčacích nástrojov alebo hotových nástrojov so zložitou dutinou by sa mal pridať proces znižovania napätia a temperovania (aby sa eliminovalo elektrické obrábanie a namáhanie pri obrábaní, to znamená, aby sa eliminovalo tepelné a organizačné napätie);
e. Mala by byť teplota kaliaceho oleja? 100 stupňov, aby sa zabezpečil zhášací účinok.